Comparative Evaluation of effect of resin protective coatings on the surface hardness and shear punch strength of different GlCs - An InVitro Study
Аннотация
G-Coat Plus is a nano-filled, self-adhesive light cured protective coating that strengthens, protects and enhances glass ionomer restorations. The effect of G- Coat plus on different GICs have not been studied comprehensively. Hence the study was conducted to compare the effect of resin coating on surface hardness and Shear punch strength of newer modified GIC.
Materials and methods: 120 samples of three GICs i.e. Fuji IX Extra, Fuji IX Fast, Fuji II LC were prepared using specialized metal moulds. Specimens of Fuji II LC were light cured for 20 seconds. Coated and uncoated samples were tested for surface hardness and 30 samples were tested for shear punch strength. P < 0.05 was considered as significant.
Results: Shear Punch Strength after G-Coat plus coating was significantly higher for Fuji IX Extra followed by Fuji II LC. Surface Hardness after G- Coat plus coating was significantly higher for Fuji IX Extra followed by Fuji IX Fast and Fuji II LC.
Conclusion: Surface coating by a resin agent significantly increases the surface hardness and shear strength of the GIC. Considering the above stated findings, they can be incorporated into daily clinical practice to enhance the strength and longevity of GIC.
Об авторах
N. Mishra
Mansarovar Dental College Hospital and Research Centre
Индия
Индия
Niharika Mishra, MDS, Assistant professor, Department of Conservative Dentistry & Endodontics
Bhopal
M. Agarwal
People's College of Dental Sciences and Research Centre
Индия
Индия
Manish Agarwal, MDS, HOD, Department of Conservative Dentistry & Endodontics
Bhopal
M. P. Singh
Chirayu Medical College and Hospital
Индия
Индия
M. P. Singh, MDS, Professor and HOD, Dentistry Department
Bhopal
A. Khullar
Rishiraj College of Dental Science and Research Centre
Индия
Индия
Apoorva Khullar, MDS, Senior Lecturer
Bhopal
K. Magwa
People's College of Dental Sciences and Research Centre
Индия
Индия
Khushboo Magwa, MDS, Assistant Professor, Department of Conservative Dentistry & Endodontics
Bhopal
S. S. Thakur
Sri Aurobindo college of dentistry
Индия
Индия
Sonal Singh Thakur, MDS, Senior Lecturer, Deparment of Conservative Dentistry & Endodontics
Indore
Список литературы
1. Lohbauer U. Dental GIC s as Perm anent Filling M aterials? - Properties, Lim itations and Future Trends. Materials. 2010; 3: 76-96.
2. Wilson A. D., Kent B. E. Surgical cem ent. British Patent No. 1316129, filed in 1969, specification published in 1973.
3. Sidhu S. K. G lass-ionom er cement restorative materials: a sticky subject? Aust Dent J. 2011 Jun; 56 Suppl 1: 23-30.
4. Sidhuyashi M., Kon M., Miyai K., Asaoka K. Strengthening of glassionom er cem ent by com pounding short fibres with CaO-P2O5-SiO2-Al2O3 glass. B iom aterials.2000; 21: 2051-8.
5. Wang, Linda, D’alpino, Lopes P.H. P., Gonzaga L, Pereira J. C. Mechanical properties of dental restorative materials: relative contribution of laboratory tests.J. Appl. Oral Sci. 2003; 11 (3): 162-167.
6. Bagheri R., Tyas M. J., Burrow M. F. Comparison of the effect of storage media on hardness and shear punch strength of tooth-colored restorative materials. Am J Dent. 2007; 20 (5): 329-34.
7. Saleh L. A., Khaiil M. F.. The Effect Of Different Protective Coatings On The Surface Hardness Of GICs. The Saudi Dental Journal. 1994: 6 (1):3-7.
8. Leirskar J., Hakon Mount N., Graham J. Ngo, Hien. The influences of resin coating on the shear punch strength of a high strength au tocure glass ionomer. Dental Materials. 2003;19 (2): 87-91.
9. Nagaraja Upadhya P., Kishore G. GIC - The D ifferent Generations, Trends Biomater. Artif. Organs 2005;18 (2): 158-165.
10. Williams J. A., Billington R. W., Pearson G. J. Effect of moisture protective coatings on the strength of a modern metal-reinforced glass-ionomer cement. J Oral Rehabil. 1998; 25 (7): 535-40.
11. Hattab F. N., Amin W. M. Fluoride release from glass ionomer restorative materials and the effects of surface coating. Biom aterials 2001; 22: 1449-1458.
12. Mount G. J., Makinson O. F. Glass-ionomer restorative cements: clinical im plications of the setting reaction. Oper Dent. 1982. Autumn; 7(4): 134-41.
13. Causton B. E. The physico-m echanical consequences of exposing GICs to water during setting. Biom aterials. 1981; 2 (2) :112-5.
14. Kato K., Yarimizu H., Nakaseko H., Sakuma T. and Corporation G. C. 2008 Abstract No. # 0487 Fuji IX GP Extra , G -Coat Plus , Fuji Coat LC , Fuji Varnish Influence of coating materials on conventional glassionom er cem ent. J. Dent. Res. 87 105377.
15. Booth S. E., Deacon A. D., Coleman N. J. Properties of GlassIonom er Cements Sealed with Petroleum Jelly or Wax. World Acad Sci Eng Technol. 2012; 6 (12): 12-26.
16. Bagheri R., Azar M. R., Tyas M. J., Burrow M. F. The effect of aging on the fracture toughness of esthetic restorative materials. Am J Dent. 2010; 23 (3): 142-6.
17. Sidhu S. K., Watson T. F. Resin-modified glass ionomer materials. A status report for the American Journal of Dentistry. Am J Dent. 1995; 8 (1): 59-67.
18. Agnihotri Y., Pragada N. L., Rama Rao S. B., Chacko Y. J. Contemp. Den. 2011; 2(5): 121-124.
19. Zhang Y. R., Du W., Zhou X. D., Yu H. Y. Review of research on the mechanical properties of the human tooth. Int J Oral Sci. 2014 Jun; 6 (2): 61-9.
20. Bala O., Hacer Deniz Arisu D. H., Yikilgan I., Arslan S., Abdulkadir Gullu. Evaluation of surface roughness and hardness of different GICs. Eur J Dent 2012; 6 (1): 79 -86.
21. Xie D., Brantley W. A., Culbertson B. M., Wang G. Mechanical properties and microstructures of glass-ionom er cements. Dental Materials. 2000; 16 (2): 129-138.
Рецензия
Для цитирования:
Mishra N., Agarwal M., Singh M.P., Khullar A., Magwa K., Thakur S.S. Comparative Evaluation of effect of resin protective coatings on the surface hardness and shear punch strength of different GlCs - An InVitro Study. Эндодонтия Today. 2021;19(3):160-165. https://doi.org/10.36377/1683-2981-2021-19-3-160-165
For citation:
Mishra N., Agarwal M., Singh M.P., Khullar A., Magwa K., Thakur S.S. Comparative Evaluation of effect of resin protective coatings on the surface hardness and shear punch strength of different GlCs - An InVitro Study. Endodontics Today. 2021;19(3):160-165. https://doi.org/10.36377/1683-2981-2021-19-3-160-165
Просмотров: 436
.jpeg)
Послать статью по эл. почте 